10-60ppi High Temperature Resistant Sic/Silicon Carbide Porous Ceramic Foam Filter for Metal Filtration Industry

• Application: Ceramic Decorations, Refractory, Structure Ceramic, Industrial Ceramic
• Speciality: Temperature Resistant
• Type: Ceramic Plates
• Material: Alumina Ceramic
• Transport Package: Wooden Case
• Specification: Customized
• Model NO.: 25mm 16mm 38mm 50mm 76mm
• Origin: China
• Production Capacity: 20000PCS Per Week

Product Description

Specifications for Alumina Casting

	Dimensions (mm)	Dimensions (inch)	Pouring Rate (kg/s)	Filtration Capacity (ton)
	178×178×50	7×7×2	0.2-0.6	5
	228×228×50	9×9×2	0.3-1.0	10
	305×305×50	12×12×2	0.8-2.5	15
	381×381×50	15×15×2	2.2-4.5	25
	430×430×50	17×17×2	3.0-5.5	35
	508×508×50	20×20×2	4.0-6.5	45
	585×585×50	23×23×2	5.0-8.6	60

Specification for Iron casting

	Dimensions (mm)	Pouring Rate (kg/s)		Filtration Capacity (kg)
		Grey Iron	Ductile Iron	Grey Iron	Ductile Iron
	40×40×22	4	3	65	32
	50×50×22	6	4	100	52
	75×50×22	9	6	150	75
	75×75×22	14	9	220	100
	100×50×22	12	8	200	100
	100×75×22	18	12	300	150
	100×100×22	25	16	400	200
	150×150×22	50	36	900	450

Specification for Steel/Magnesium casting
Specification for Steel/Magnesium casting

Dimensions (mm)	Zirconia Foam Filter		Dimensions (mm)	Magnesia Foam Filter
	Pouring Rate(kg)	Filtration Capacity(kg)		Pouring Rate(kg)	Filtration Capacity(kg)
50×50×22	3~5	30	Ф50×22	4.0	60
50×75×22	4~6	40	Ф60×22	7.0	80
75×75×22	7~12	60	Ф90×22	10.0	120
75×100×22	8~15	80	Ф120×22	16.0	160
100×100×22	14~20	100	100×100×22	13.0	140
Ф50×22	2~6	18	150×150×25	22.0	260
Ф80×22	6~10	50	230×230×30	130.0	3100
Ф90×22	8~16	70	300×300×40	260.0	5200

Physical and chemical properties
 

Material	Alumina	Silicon Carbide	Zirconia
Color	White	Grey black	Yellow
Pore Density	10-60ppi	10-30ppi	10-30ppi
Porosity	80-90%	80-90%	80-90%
Refractoriness	≤1100ºC	≤1500ºC	≤1700ºC
Bending Strength	>0.6Mpa	>0.8Mpa	>1.0Mpa
Compression Strength	>0.8Mpa	>0.9Mpa	>1.2Mpa
Volume-weight	0.3-0.45g/cm^3	0.35-0.5 g/cm^3	0.9-1.5 g/cm^3
Thermal shock resistance	6 times/1100ºC	6 times/1100ºC	6 times/1100ºC
Application	Aluminium, Aluminium alloys and other Non-ferrous alloys	Ductile Cast Iron, Malleable Cast Iron, Gray iron and other Cast Iron	High melting point metal alloys like Steel, Alloy Steel, Stainless Steel etc
Chemical Composition	Al3O2> 80% SiO2< 10%	SiC≥60% Al2O3≤30% SiO2≤10%	ZrO2≥ 94% Al2O3≤1.8% MgO≥3.0% SiO2≤0.5% Fe2O3≤0.10%